Great size and shape for that single knife quiver. If you only buy one knife, make it this one.
SHAPE: Gyuto. Literally translates as "cow sword", this is Japan's answer to the western chef knife.
STEEL: Shirogami (white paper) 1 steel. This steel has the highest amount of carbon out of the paper steels so will get crazy sharp easily. It is a very reactive steel so best kept dry although the kurouchi finish will help inhibit rust.
Shirogami 1 is a lot easy to sharpen and theoretically you can get it sharper. By contrast, Aogami 2 has better edge retention and is slightly less susceptible to rusting. The choice is yours!
FINISH: Kurouchi. This is a traditional, rustic finish achieved by leaving the furnace scale from the forging process on the blade rather than polishing it off. It has the advantage of reducing the reactivity of the surface of the knife and gives the blade a stylish, matt black finish. This blade has also had a lacquer applied to it which will further inhibit rust, over time it will slowly come off. It is worth noting that during the application process some of the lacquer can be applied to the edge masking its sharpness. This can be removed using a sharpening stone or by very lightly drawing it across a fine steel, preferably a ceramic one.
HANDLE: Octagonal walnut wood handle with pakka wood ferrule suitable for both lefties and righties.
LENGTH: 210 0r 240 mm
MAKER: Yamashin - Takefu, Japan
BEST FOR: Everything.
SAUNDERS SAYS: "Like all the other knives in this range it sharpens like a dream and has great edge retention"
BLADE LENGTH: 219mm
OVERALL LENGTH: 372mm
BLADE HEIGHT: 52mm
THICKNESS AT HEEL: 3.3mm this quickly tapers down the blade
These knives are hand-forged so there may be slight variations in measurements and finishes.
General Knife care instructions
There are a basic set of rules that you should adhere to. If you come into store, we will discuss these with you at length alongside other tips and tricky to get the best from your knife. We also give you a little card as a reminder and which also gives you your first sharpen free of charge.
- ALWAYS CUT ON A WOOD OR PLASTIC CHOPPING BOARD: Because continually hitting the edge of your knife onto a hard surface will blunt it and risks chipping the edge. This should go without saying as glass chopping boards will not only blunt your knives but are also a complete abomination. Also try to avoid cutting directly on plates. If you are super keen, try a hi-soft chopping board (we sell these in store) or a hinoki board.
- RINSE AND DRY AFTER USE: If it is carbon steel, you don't want to keep it wet as this will risk rust developing. Keep a tea towel next to your board and just wipe off the knife from time to time. Don't be an animal, clean your knife.
- NEVER PUT IN THE DISHWASHER OR LEAVE TO SOAK: Putting knives in the dishwasher blunts them. Yes, chefs, this includes giving it to the KP to run through the pot wash. Don't do it! All you need to do is hold the knife tip down under the tap, rinse it off and dry it. Knives don't really get that dirty and you want to avoid water getting in and around the handle. Any soaking or dishwashering also damages the glues in the handle. This is the absolute unquestionable indisputable no no.
- AVOID TWISTING OR PRYING MOTIONS: If you put stress on a fine edge of a knife it will chip. This might not happen straightaway but the risk of damaging the knife is definitely there. Things to avoid include hacking into butternut squash, hitting into the stone of an avocado, chopping through a chicken carcass, or, god forbid, trying to open oysters. If in doubt, don't do it. Have a rubbish second rate cheap knife and do any gnarly jobs - where you are reliant on brute force rather than precision sharpness - with this. Steel doesn't just randomly fall apart or shatter but if you stress the edge it will eventually chip.
- CARBON STEEL WILL DEVELOP A PROTECTIVE PATINA AFTER USE. WIPE AFTER USE OR AFTER CUTTING ANYTHING ACIDIC TO AVOID RUST FORMING: a protective patina is a dark grey in colour. It is not orange. Rust is orange. As the patina develops, the surface will become less reactive and the knife easier to care for. If you have by accident allowed it to rust, don't worry, this can be removed.
- DO NOT SHARPEN ON A METAL STEEL: This should read, don't "TRY" to sharpen on a metal steel. Steels don't remove metal and sharpen knives, they just realign the edge. Don't go at one with your knife in a swashbuckling fashion, this is likely to chip the knife at worst and, at best, will remove the metal unevenly, therefore making it harden to sharpen. Steels should be used gently and sparingly, if you aren't sure what you are doing with one, don't!
- STORE IN BOX OR ON KNIFE RACK: As you might be gathering by now, knife against anything hard is potentially damaging. This includes letting it rattle round in your cutlery drawer. We also aren't big fans of concealed knife blocks as you don't really know where you are sticking it. You can't go wrong keeping it in its box or, if possible, a wall mounted knife rack with some sort of cushioning (rubber or wood).